HARRIS 0 phos-copper-copper brazing alloy is a low cost alloy use for many copper-to-copper applications where moderate fit-up can be maintained and brazing temperature is not critical. Conforms to the EU Reach & RoHS directive.
Features
- Economical choice for copper brazing
- Copper is self-fluxing
- Alloy flows quickly at brazing temperature so requires close joint tolerance of less than 0.005 in. (0.13 mm)
- Primarily used in manual brazing applications
- Suitable for brazing brass
- Operators should avoid overheating the brass and use Stay-Silv white brazing flux
- Not recommended for brazing steel or other ferrous base metals
- Should not use Harris 0 if braze is exposed to sulfur or sulfur compounds in service
- Recommended joint clearance of 0.002 in. - 0.007 in. (0.05 mm - 0.18 mm)
- Complies with the EU Reach & RoHS directive
Typical Applications
- Copper-to-copper joint brazing
- Brass joint brazing